AURAPENE PPUFBK
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Aurora Manufacturing Ltd |
| Trademark: | AURAPENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qLcVOz_AURAPENE-PPUFBK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPUFBK is a general purpose polypropylene compound manufactured from recycled polymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 to 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.3 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 to 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 10 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 100 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Rear Temperature | 195 to 230 | °C | |
| Middle Temperature | 195 to 230 | °C | |
| Front Temperature | 195 to 230 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4003EPG20 | POLYROCKS CHEMICAL CO., LTD | Nylon 66 | PONYL |
| REXtac® APAO RT 1230 | Huntsman Corporation | PAO | REXtac® APAO |
| Sylvin RP 3107 Clear 8414 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ACLAR® 88A | Honeywell | PCTFE | ACLAR® |
| Abstron KU602M | Bhansali Engineering Polymers Limited | ABS | Abstron |