Order Products : sales@su-jiao.com
MAJ'ECO EG368LA
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qIzkLQ_MAJ-ECO-EG368LA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO EG368LA is a glass fibre reinforced Biopolymer compound intended for injection moulding. MAJ'ECO EG368LA has been developed especially for demanding applications in various engineering sectors. MAJ'ECO EG368LA has high rigidity, good dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 104 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 9150 | MPa | ISO 178 |
| Flexural Stress 2 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 116 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 59.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 FLBK | Nilit Plastics | Nylon 66 | POLYNIL® |
| ProvaMed® PVC 3240 | ACTEGA GmbH | PVC, Unspecified | ProvaMed® PVC |
| Ketjenflex® 4 | Axcentive SARL | Plasticizer | Ketjenflex® |
| Pebax® 3533 SD 01 | Arkema | PEBA-Ether | Pebax® |
| Sylvin 8381-75 Brown 7438 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |