Riteflex® 663
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Riteflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qGoV3f_Riteflex-663.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Riteflex 663 is a nominal 63 Shore D thermoplastic polyester elastomer with medium modulus. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.820 | cm³/g | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ross Flex | > 1.0E+6 | Cycles | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 269.7 | kN/m | ASTM D1004 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | |||
| -- | 16 | g/10 min | ASTM D1238 |
| 240°C/2.16 kg | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.9 | % | ASTM D955 |
| Vertical flow direction | 1.7 - 2.1 | % | ISO 294-4 |
| Flow direction | 1.7 - 2.0 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shaw D | 63 | ASTM D2240 | |
| Shaw D, 15 seconds | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 365 | MPa | ASTM D638 |
| -- | 350 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 22.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 23°C | 26.2 | MPa | ASTM D638 |
| Fracture | 38.0 | MPa | ISO 527-2/1A/50 |
| 5.0% strain | 13.0 | MPa | ISO 527-2 |
| 10% strain | 18.0 | MPa | ISO 527-2 |
| 50% strain | 21.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | |||
| Yield | 44 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 320 | % | ASTM D638 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus | ISO 178 | ||
| -40°C | 1900 | MPa | ISO 178 |
| 23°C | 325 | MPa | ISO 178 |
| Flexural Stress (23°C) | 17.5 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | |||
| -- | 266 | kN/m | ASTM D624 |
| Flow 1 | 160 | kN/m | ISO 34-1 |
| Compression Set (23°C) | < 1.0 | % | ASTM D395 |
| Bayshore Resilience | |||
| -- | 40 | % | Internal method |
| -- | 40 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 22 | kJ/m² | ISO 179/1eA |
| 23°C, local fracture | 110 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 74 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 114 | °C | ISO 75-2/B |
| Glass Transition Temperature | -42.8 | °C | ASTM D3418 |
| Vicat Softening Temperature | 195 | °C | ASTM D1525 |
| Melting Temperature | |||
| -- 2 | 212 | °C | ISO 11357-3 |
| -- | 210 | °C | ASTM D3418 |
| CLTE - Flow | 1.8E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 2.0E+13 | ohms·cm | ASTM D257 |
| -- | 2.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 13 | kV/mm | ASTM D149 |
| -- | 14 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.040 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 200 - 215 | °C | |
| Middle Temperature | 215 - 230 | °C | |
| Front Temperature | 215 - 230 | °C | |
| Nozzle Temperature | 215 - 235 | °C | |
| Processing (Melt) Temp | 215 - 235 | °C | |
| Mold Temperature | 20.0 - 55.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 215 to 235°CZone 4 Temperature: 215 to 235°CFeed Temperature: 200 to 215°C |
| Note Message | |
|---|---|
| 1 . | Die C |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 5120N | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Braskem PE SLL118 | Braskem | LLDPE | Braskem PE |
| Hanwha Total PP HS120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| HiFill® TPX-HTN-03003 A | Techmer Engineered Solutions | Nylon, Unspecified | HiFill® |
| Kepamid® 1825GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |