NOVAPOL® PF-Y818-FX
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qGkLSs_NOVAPOLPFY818FX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL®PF-Y818-FX is a linear low density polyethylene material,. This product is available in North America and is processed by film extrusion or blow molding. NOVAPOL®The main features of the PF-Y818-FX are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | > 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 175 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 230 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 47.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 33.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 810 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 50 | g | ASTM D1922 |
| TD : 25 µm, blown film | 480 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture 1(25.0 µm) | 840 | J/cm | Internal method |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom W17030LT-105 | Spartech Polycom | PVC Alloy | Spartech |
| Multi-Flam™ 0803 | Multibase, A Dow Corning Company | LDPE | Multi-Flam™ |
| Infino VB-5300G | SAMSUNG SDI CO., LTD. | PBT | Infino |
| Karina WHITE PVC COMPOUND 920-10/156-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent TPO TPO-30T | Lucent Polymers, Inc. | Polyolefin, Unspecified | Lucent TPO |