Wanthane® WHT-1164IC
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qGH8Ck_WanthaneWHT1164IC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyester-based grade Extrusion and injection molding grade FEATURES: Excellent mechanical properties, high abrasion resistance, good wear resistance, short cycle times Applications: Shoe heels, Injection-molded engineering components, wire & cable, etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 45.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 26.0 | MPa | ASTM D412 |
| 300% strain | 40.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 45.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 340 | % | ASTM D412 |
| Tear Strength | 225 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 24 hr | 25 | % | ASTM D395 |
| 70°C, 22 hr | 68 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -9.00 | °C | ASTM D3418 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 205 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 215 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 195 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Adapter Temperature | 205 | °C | |
| Die Temperature | 195 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 A | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Ultramid® 8255 HS | BASF Corporation | Nylon 6 | Ultramid® |
| AKROMID® B3 2 S3 natural (4018) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Iupilon® GS2010MN1 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ THERMOCOMP™ EC006 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |