SPECIALTY PPA COMPOUND
PPA, 30% GLASS FIBER REINFORCED, HEAT STABILIZED |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow : 23°C | 0.70 | % | ISO 294-4 |
| Flow : 23°C | 0.30 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 150 | MPa | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.2 | kJ/m² | ISO 179/1eA |
| 23°C | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 275 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | IEC 60216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 21 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.40 mm | HB | UL 94 | |
| 0.8 mm | HB | UL 94 | |
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 20 V25 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| VECTRA® MT1300 | Celanese Corporation | LCP | VECTRA® |
| Kingfa API-230 | Kingfa | PP, Unspecified | Kingfa |
| Hyundai EP PPF HT940 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| RONFALIN® ASA 3324 U | A. Schulman Europe | ASA | RONFALIN® |