ProvaMed® TPE 1158
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ACTEGA GmbH |
| Trademark: | ProvaMed® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qFUABg_ProvaMed-TPE-1158.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ProvaMed® TPE 1158 is a Thermoplastic Elastomer (TPE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of ProvaMed® TPE 1158 are:
Typical application of ProvaMed® TPE 1158: Medical/Healthcare |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 35 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 5 sec | 58 | ||
| Shore D, 5 sec | 12 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 2.00 | MPa | DIN 53504 |
| Tensile Stress (Yield) | 5.40 | MPa | DIN 53504 |
| Tensile Elongation (Break) | 1100 | % | DIN 53504 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 23 | % | |
| 70°C, 22 hr | 89 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | -57.0 | °C | DSC |
| Melting Temperature (DSC) 2 | 151 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 20.0 to 30.0 | °C | |
| Rear Temperature | 140 to 210 | °C | |
| Middle Temperature | 140 to 210 | °C | |
| Front Temperature | 140 to 210 | °C | |
| Nozzle Temperature | 180 to 220 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Heating rate 10 K/minMelting peak from second heating cycle |
| 2 . | Heating rate 10 K/minMelting peak from second heating cycle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS 1002 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Naturacell® General | Rotuba Extruders, Inc. | CA | Naturacell® |
| NORYL™ 6390H resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| TECACOMP® PBT TF natural 3438 | Ensinger GmbH | PBT | TECACOMP® |
| ZEONEX® 5000 | Zeon Corporation | COP | ZEONEX® |