DENKA ABS K-5110G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qFTwNF_DENKA-ABS-K-5110G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DENKA ABS K-5110G is an Acrylonitrile Butadiene Styrene (ABS) product filled with 10% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| 23°C | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 0.60 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.20 to 0.40 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 120 | ASTM D785 | |
| R-Scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 58.0 | MPa | ASTM D638 |
| -- | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 58.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 3550 | MPa | ASTM D790 |
| -- 3 | 3800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 93.0 | MPa | ASTM D790 |
| -- 5 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 6 | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 129 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ASTM D1525 7 |
| -- | 135 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 15 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 15 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Edgewise |
| 7 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® Endure D5G3 BM BK20560 | BASF Corporation | Nylon 66 | Ultramid® |
| Nymax™ GF1200 A13 HS NC067 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Fainplast PVC MPH 62/H | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Forprene® 6NM919A60 | SO.F.TER. SPA | TPV | Forprene® |
| Mafill® CF 4010 | Ravago Group | PP Copolymer | Mafill® |