Order Products : sales@su-jiao.com
Aaroprene® ATPR 2000 80A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Aaron Industries Corp. |
| Trademark: | Aaroprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qFDcBE_Aaroprene-ATPR-2000-80A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aaroprene®ATPR 2000 80A is a thermoplastic elastomer (TPE) material,. This product is available in North America and is processed by film extrusion, extrusion or injection molding. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 - 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2.07 | MPa | ASTM D412 |
| Taber Abrasion Resistance (1000 Cycles, H-18 Wheel) | 110 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 11.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength 1 | 58.7 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 79.4 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 227 | °C | |
| Nozzle Temperature | 235 | °C | |
| Injection Pressure | 3.45 - 4.83 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 40 | rpm |
| Injection instructions |
|---|
| Injection Time: 1 secHold Time: 5 secClamp Time: 7 secCycle Time: 15 sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 79.4 | °C | |
| Cylinder Zone 2 Temp. | 191 | °C | |
| Cylinder Zone 3 Temp. | 191 | °C | |
| Cylinder Zone 4 Temp. | 191 | °C | |
| Cylinder Zone 5 Temp. | 191 | °C | |
| Melt Temperature | 191 - 246 | °C | |
| Die Temperature | 235 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 24:1Low Compression RatiosDeep Flighted Metering SectionsFilm Extrusion Melt Temperature: 400 to 475°F |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® M525 | Covestro - Polycarbonates | PC+PBT | Makroblend® |
| SAMAT EP5001A(f1) | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Bayflex® XGT-2 | Covestro - PUR | PUR-MDI | Bayflex® |
| Catalyst F/AC | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Sumikon® PM-6630 (Type: Black) | SBHPP | Phenolic | Sumikon® |