Order Products : sales@su-jiao.com
Generic PI, TP
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qERVE2_Generic-PI-TP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PI, TP This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.31 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 1.31 - 1.52 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 4.0 - 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.89 - 1.1 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.60 - 0.62 | % | ASTM D570 |
| Saturated, 23°C | 2.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3390 - 3880 | MPa | ASTM D638 |
| 23°C | 3100 - 10500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 103 - 156 | MPa | ASTM D638 |
| Yield, 23°C | 101 - 147 | MPa | ISO 527-2 |
| Fracture, 23°C | 96.0 - 156 | MPa | ASTM D638 |
| Fracture, 23°C | 70.0 - 147 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 - 9.1 | % | ASTM D638 |
| Yield, 23°C | 2.0 - 9.0 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 20 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 19 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2760 - 8960 | MPa | ASTM D790 |
| 23°C | 2850 - 3000 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 150 - 200 | MPa | ISO 178 |
| Yield, 23°C | 168 - 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 - 24 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 42 - 87 | J/m | ASTM D256 |
| 23°C | 4.2 - 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 250 - 264 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 233 - 256 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 224 - 233 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 257 - 267 | °C | ASTM D1525 |
| -- | 248 - 263 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 1.6E-5 - 5.7E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.6E-5 - 4.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 4.7E-5 - 5.3E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.4E+12 - 1.4E+16 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 8.2E+13 - 1.4E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 41 - 310 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 370 - 385 | °C | |
| Middle Temperature | 383 - 398 | °C | |
| Front Temperature | 392 - 405 | °C | |
| Nozzle Temperature | 388 - 405 | °C | |
| Processing (Melt) Temp | 393 - 408 | °C | |
| Mold Temperature | 163 - 164 | °C | |
| Screw Speed | 55 - 85 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PI, TPThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DURAFIDE® 1140A1 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |
| Geon™ Vinyl Flexible C8009 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| KumhoSunny PC 2501FR | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Pearlthane® CLEAR 15N70 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |
| Polaris™ MR 80499-18 | Ashland Performance Materials | Polyester, TS | Polaris™ |