Kingfa PA6-M20G16
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qCzD43_Kingfa-PA6-M20G16.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PA6-M20G16 is a polyamide 6 (nylon 6) material, which contains 20% glass fiber reinforced materials and 16% mineral fillers. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PA6-M20G16 are:
The typical application field of Kingfa PA6-M20G16 is: automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 110 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus 3 | 7800 | MPa | ASTM D790 |
| Flexural Strength 4 | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 218 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 208 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 225 - 245 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 255 - 285 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 300°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILAC AE8000 | Formosa Plastics Corporation | ABS | TAIRILAC |
| NITRIFLEX NP-2174 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| InnoPlus HD8000F | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Jazz® 001 | PolyPacific Pty. Ltd. | PP, Unspecified | Jazz® |
| Petrothene® NA952094 | LyondellBasell Industries | LDPE | Petrothene® |