EC401 - 8229 is a black, 40% mineral filled polypropylene compound intended for injection moulding. The product is available in natural (EC401) and black (EC401 - 8229) but other colours can be supplied on request. EC401 - 8229 is intended for component, which require good surface quality and high heat stabilised properties, rigidity, low shrinkage and high dimensional stability. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 37 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 113 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 62.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A |
| -- | 100 | °C | ISO 306/B |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD1090 | Qenos Pty Ltd | HDPE | Qenos PE |
| SEETEC EVA VA900 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| ALKAMIX™ MB-6009 | Marplex Australia Pty. Ltd. | Unspecified | ALKAMIX™ |
| LG PMMA IH830HR | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| LONGLITE® PBT 6030-104X | CCP Group | PC+PBT | LONGLITE® PBT |