Order Products : sales@su-jiao.com
KumhoSunny PET HEG3630
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qB6Mvm_KumhoSunny-PET-HEG3630.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEG3630 is a 30% glass fiber reinforced, modified polyethylene terephtalate for injection molding. offering high rigidity,high heat resistance, good surface quality and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.60 | g/cm³ | ASTM D792 |
| -- | 1.58 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.80 | % | ASTM D955 |
| -- | 0.60 to 1.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 150 | MPa | ASTM D638 |
| -- | 130 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 11000 | MPa | ASTM D790 |
| -- 1 | 8500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 250 | MPa | ASTM D790 |
| -- 2 | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Notched Izod Impact | |||
| 3.20 mm | 100 | J/m | ASTM D256 |
| 23°C | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 230 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 3 | 225 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 245 to 260 | °C | |
| Middle Temperature | 250 to 265 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 245 to 275 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9135 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SEALUTION™ 220 | The Dow Chemical Company | EPE | SEALUTION™ |
| G-PAEK™ 1200P | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Karina WHITE PVC COMPOUND -E TR-556D10/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lushan M-12A | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |