Braskem PE IDEALIS500
| Category: | HMWPE , High Molecular Weight Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qAsyig_Braskem-PE-IDEALIS500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: Braskem Idealis500 is the only High Molecular Weight Polyethylene resin in powder form specially designed for the compression molding process. Applications: Applications range from food handling cutting boards and playground toys to technical parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Apparent Density | 0.45 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.70 | g/10 min | ASTM D1238 |
| Average Molecular Weight | 550000 | g/mol | Internal Method |
| Average Particle Size 1 | 170 | µm | |
| Intrinsic Viscosity | 4.7 | dl/g | ASTM D4020 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Abrasion Index 2 | 80 | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | > 20.0 | MPa | |
| Break | > 30.0 | MPa | |
| Tensile Elongation (Break) | > 500 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | > 50 | kJ/m² | ISO 11542-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 4 |
| Melting Temperature | 136 | °C |
| Note Message | |
|---|---|
| 1 . | Dp50 |
| 2 . | reference PE500 = 100 |
| 3 . | Determined with double-notched specimens (14° v-notch on both sides) in accordance with ISO 11542-2 |
| 4 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GPT-45B2-H1 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| tefanyl® VE VEIP 250 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| DynaMix™ 475-AFR | Polymer Dynamix | LDPE | DynaMix™ |
| LNP™ STAT-KON™ REP349 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Piolen® P B50A19 | PiO Kunststoffe GmbH & Co KG | PP Homopolymer | Piolen® P |