LNP™ KONDUIT™ PX11313 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q9oM5m_LNP-KONDUIT-PX11313-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive mineral filled PA6 FR compounding Also known as: LNP* KONDUIT* Compound PX11313 Product reorder name: PX11313 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.42 | % | |
| Across Flow : 24 hr | 0.58 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.23 | % | Internal Method |
| 23°C, 24 hr | 0.040 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13300 | MPa | ASTM D638 |
| -- | 13300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 98.0 | MPa | ASTM D638 |
| Break | 110 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.3 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 12500 | MPa | ASTM D790 |
| -- 5 | 13000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 186 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 167 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 176 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.4 to 27 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256 |
| 23°C 8 | 3.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 9 | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 227 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 228 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 6.40 mm | 215 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 206 | °C | ISO 75-2/Af |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831 | ||
| Flow : 40 to 120°C | 4.1E-5 | cm/cm/°C | |
| Transverse : 40 to 120°C | 8.5E-5 | cm/cm/°C | |
| Thermal Conductivity | |||
| -- 12 | 1.4 | W/m/K | ASTM E1461 |
| -- 13 | 1.8 | W/m/K | ASTM E1461 |
| -- 14 | 0.90 | W/m/K | ISO 22007-2 |
| -- 15 | 1.9 | W/m/K | ISO 22007-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (1.00 mm, in Oil) | > 10 | kV/mm | ASTM D149 |
| Dielectric Constant (1.10 GHz) | 4.84 | ASTM ES7-83 | |
| Dissipation Factor (1.10 GHz) | 9.9E-3 | ASTM ES7-83 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 750 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 85.0 to 100 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 20 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| 12 . | through-plane, 10*10*3mm sample |
| 13 . | in-plane, ø25*0.4mm disc |
| 14 . | through-plane, ø80*3mm discs |
| 15 . | in-plane, ø80*3mm discs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F200A (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| CALIBRE鈩?2061-10 | Trinseo | PC | CALIBRE™ |
| Cheng Yu N6GV15 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Clariant Nylon 6/6 PA-113G33C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LNP™ THERMOCOMP™ BF004 compound | SABIC Innovative Plastics | SAN | LNP™ THERMOCOMP™ |