PRL TP-FR-G30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q9n3ER_PRL-TP-FR-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-FR-G30 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 9.0 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 121 | MPa | |
| Break, 3.18 mm | 121 | MPa | |
| Flexural Modulus (3.18 mm) | 9650 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 199 | °C | |
| RTI Elec | UL 746 | ||
| 0.850 mm | 140 | °C | |
| 1.60 mm | 140 | °C | |
| 2.30 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.850 mm | 130 | °C | |
| 1.60 mm | 130 | °C | |
| 2.30 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Str | UL 746 | ||
| 0.850 mm | 140 | °C | |
| 1.60 mm | 140 | °C | |
| 2.30 mm | 140 | °C | |
| 3.00 mm | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.850 mm) | 23 | kV/mm | ASTM D149 |
| Arc Resistance (0.850 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (0.850 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.850 mm | PLC 0 | ||
| 1.60 mm | PLC 0 | ||
| 2.30 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) (0.850 mm) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.850 mm | PLC 3 | ||
| 1.60 mm | PLC 2 | ||
| 2.30 mm | PLC 2 | ||
| 3.00 mm | PLC 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.850 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 2.30 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® 46HF5041LW | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| NEOPLAST 145 FT EB | Zylog Plastalloys | TPV | NEOPLAST |
| Plenco 01581 (Injection) | Plastics Engineering Co. | Polyester, TS | Plenco |
| Hostacom HBC 309 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ STAT-KON™ CD000I compound | SABIC Innovative Plastics | PS (HIPS) | LNP™ STAT-KON™ |