Rilsan® HT CESVO P223 TL
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® HT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q8Cp0x_Rilsan-HT-CESVO-P223-TL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® HT CESVO P223 TL is a flexible polyphthalamide produced from a renewable source, typically used to replace metal in tubing for high-temperature automotive, transportation and other demanding technical applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 3.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 130 | % | ISO 527-2 |
| Flexural Modulus | 520 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 9.0 | kJ/m² | |
| 23°C | 76 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hoop Stress | |||
| 23°C | 18.0 | MPa | |
| 150°C | 3.50 | MPa | |
| Renewable Carbon Conent | 38 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Melt Temperature | 270 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® XT1627-WBK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Leona™ 91G60 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LNP™ LUBRICOMP™ KP002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| MAJORIS DW434X/8 | AD majoris | PP, Unspecified | MAJORIS |
| POLYFORT® FPP 22 T LE K1684 | A. Schulman Europe | PP Homopolymer | POLYFORT® |