Petrothene® KR52828E
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q6zXXI_Petrothene-KR52828E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petrothene KR52828E is a multi-modal, broad molecular weight high density polyethylene-based compound designed for use in jacketing, conduit or wire insulation. Petrothene KR52828E contains a robust additives package for thermal stabilisation and carbon black for UV stabilization. This grade is not intended for use in medical or pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | |
| 190°C/5.0 kg | 1.1 | g/10 min | |
| Environmental Stress-Cracking Resistance (F0) | > 2000 | hr | ASTM D1693 |
| Carbon Black Content | 2.3 | % | ISO 6964 |
| Moisture Content 1 | 0.050 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 30 | min | ISO 11357-6 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 130 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Electric Strength | 20 | kV/mm | IEC 60243-1 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | VP608B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowital® B 20 H | Kuraray Co., Ltd. | PVB | Mowital® |
| Geon™ Vinyl Rigid Extrusion L0678 Natural | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Eltex® PF1315AA | INEOS Olefins & Polymers Europe | MDPE | Eltex® |
| Latilub 37 B01-02S | LATI S.p.A. | PLA | Latilub |
| Karina GRAY PVC COMPOUND 750-18/329-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |