SABIC® STAMAX 30YK270 resin
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® STAMAX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q6yEM2_SABIC-STAMAX-30YK270-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® STAMAX 30YK270 is a 30% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 80929807. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| -- | 6200 | MPa | ISO 527-2/1 |
| 80°C | 4400 | MPa | ISO 527-2/1 |
| 120°C | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Fracture | 98.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 80°C | 60.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 120°C | 43.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/50 |
| Flexural Modulus 1 | ISO 178 | ||
| 64.0mm span | 5500 | MPa | ISO 178 |
| 80°C, 64.0mm span | 3600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 24 | kJ/m² | ISO 179/1eA |
| 23°C 3 | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | 70 | kJ/m² | ISO 179/1eU |
| 23°C | 57 | kJ/m² | ISO 179/1eU |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load 5 | 5.70 | J | ASTM D3763 |
| 23°C, energy to peak power 6 | 5.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7(1.8 MPa, Unannealed) | 157 | °C | ISO 75-2/A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Fiber Content | 30 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 290 | °C | |
| Middle Temperature | 225 - 285 | °C | |
| Front Temperature | 220 - 280 | °C | |
| Nozzle Temperature | 220 - 280 | °C | |
| Processing (Melt) Temp | 220 - 280 | °C | |
| Mold Temperature | 20.0 - 80.0 | °C | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Screw Speed: Lowest Possible |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 6.60 m/sec |
| 6 . | 6.6 m/sec |
| 7 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toughblend® PA66-1303 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| AKROMID® A3 4 S1 black (2895) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| CGPC PVC SO-30X (105 phr Plasticizer E) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| K-Resin® SBC KK38 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |
| LNP™ THERMOCOMP™ DX11355 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |