Medalist® MD-315
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q5v6lt_Medalist-MD-315.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is designed for overmold to nylon. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.8 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 1.52 | MPa | ASTM D412 |
| 200% strain | 2.21 | MPa | ASTM D412 |
| 300% strain | 2.93 | MPa | ASTM D412 |
| Tensile Strength (Break) | 4.83 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength | 25.4 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 18 | % | ASTM D395 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to Nylon |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 193 - 216 | °C | |
| Middle Temperature | 260 - 282 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Nozzle Temperature | 282 - 302 | °C | |
| Processing (Melt) Temp | 282 - 302 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Moisture can degrade the material. Drying is suggested. This can be accomplished by placing the material in a desiccant dryer for 2 to 4 hours at 140°F. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 216 | °C | |
| Cylinder Zone 2 Temp. | 249 - 271 | °C | |
| Cylinder Zone 3 Temp. | 260 - 282 | °C | |
| Cylinder Zone 5 Temp. | 271 - 293 | °C | |
| Die Temperature | 271 - 293 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201A HI | RTP Company | Nylon 6 | RTP |
| SABIC® HDPE PCG4906 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Celanex® 6500HF | Celanese Corporation | PBT | Celanex® |
| EMERGE™ PC 4701-15 | Trinseo | PC | EMERGE™ |