LNP™ LUBRICOMP™ AL003 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q5QEeu_LNP-LUBRICOMP-AL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound AL-4030 Product reorder name: AL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.31 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2290 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 35.9 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2 |
| Break | 32.4 | MPa | ASTM D638 |
| Break | 32.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.3 | % | ASTM D638 |
| Yield | 2.7 | % | ISO 527-2 |
| Break | 15 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2060 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 62.1 | MPa | ASTM D790 |
| -- | 61.9 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.22 | ||
| vs. Itself - Static | 0.11 | ||
| Wear Factor - Washer | 100 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 3 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 8.23 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 77.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 81.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 200 H | RTP Company | Nylon 66 | RTP |
| Beetle® PET100 | Teknor Apex Company (Chem Polymer) | PET | Beetle® |
| KRALASTIC® KU-611 R-1 | Nippon A&L Inc. | ABS | KRALASTIC® |
| INEOS LDPE 24W930 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| Sylvin 9077-90LMW Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |