Sarlink® TPE ML-1240D BLK 111
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q45aMu_Sarlink-TPE-ML-1240D-BLK-111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE ML-1240D BLK 111 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The typical application field of TPE ML-1240D BLK 111 is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 46 | ASTM D2240 | |
| Shaw D, 5 seconds | 43 | ASTM D2240 | |
| Shaw D, 10 seconds | 40 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C) | 210 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 730 | % | ASTM D412 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell EP274P | LyondellBasell Industries | PP Impact Copolymer | Purell |
| COPYLENE® CH043EW | Phillips 66 | PP Homopolymer | COPYLENE® |
| Lotader® HX8290 | Arkema | EAA | Lotader® |
| 3M™ Dyneon™ PTFE Compound TF 6712 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| SQUARE® SEP8660-40 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |