Shinko-Lac® ABS TR-2
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q3qzkE_Shinko-Lac-ABS-TR-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS TR-2 is a high heat resistant grade of ABS that also features good processability, good flow and excellent mechanical properties. Typical applications of TR-2 include car radio components, name plates and automotive glove boxes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.4 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 47.1 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 72.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 49 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 97.0 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 200 - 250 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 200 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Armlen® PP TM 15-1AP | Poly Plastic | PP, Unspecified | Armlen® |
| Aurora PVC AP1250T | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Edgetek™ UR2-40CF/000 BLACK | PolyOne Corporation | PUR, Unspecified | Edgetek™ |
| Plaslube® PC / ABS 8800 | Techmer Engineered Solutions | PC+ABS | Plaslube® |
| CYCOLAC™ MG47U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |