Elastollan® C78A15
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | q3Q3FE_Elastollan-C78A15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® C78A exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C78A is rated UL-94 HB in vertical flame test for wall thickness of 0.9 mm. Elastollan® C78A is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 to 30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 19.3 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 21.4 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 25.0 | mg | ASTM D1044 |
| Abrasion - DIN | 15 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 85 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 5.52 | MPa | |
| 300% Strain | 11.7 | MPa | |
| Tensile Strength | 37.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 680 | % | ASTM D412 |
| Tear Strength 1 | 94.6 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 35 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -41.0 | °C | Internal Method |
| Vicat Softening Temperature | 79.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.900 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E885 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| TPSiV™ 3040-70A BLK 25349 | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Yuyao PPO SE1X701 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| TechnoDur PBT/PET GF 15 Natural (9972) | TechnoCompound GmbH | PBT+PET | TechnoDur |
| Sylvin 4200-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |