Noryl* FE1410PW resin is a blend of polyphenylene Oxide (PPO) and polystyrene (PS) resin that contains 10% glass reinforcement. The resin is suitable for injection molding. Noryl FE1410PW resin has been developed for fluid engineering applications that require improved hydrolytic stability. Noryl FE1410PW resin has been certified for potable water applications up to 85C in Europe and North America in limited colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 32.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 - 0.40 | % | Internal method |
| Water Absorption | |||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Balance, 50% RH | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4780 | MPa | ASTM D638 |
| -- | 4930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 94.0 | MPa | ASTM D638 |
| Fracture | 94.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.8 | % | ASTM D638 |
| Fracture | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 4860 | MPa | ASTM D790 |
| -- 5 | 4880 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 135 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | ISO 179/1eU |
| 23°C | 14 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 35 | J/m | ASTM D256 |
| -30°C 8 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 230 | J/m | ASTM D4812 |
| 23°C | 230 | J/m | ASTM D4812 |
| -30°C 10 | 13 | kJ/m² | ISO 180/1U |
| 23°C 11 | 13 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 12 | 135 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 127 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 126 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 146 | °C | ISO 306/A50 |
| -- | 140 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers A3 PRTA010 65A IM06S1 UP338 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Zenite® 7755 | Celanese Corporation | LCP | Zenite® |
| Andur M-33 (DEG) | Anderson Development Company | PUR-Ester/MDI | Andur |
| ESTOPLAST XU 425 HG36 | Ester Industries Ltd. | Nylon, Unspecified | ESTOPLAST XU |
| Sylvin 83028-90 Orange 5112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |