Toyolac® 100G-20
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pz4qC3_Toyolac100G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac®100G-20 is an acrylonitrile butadiene styrene (ABS) material, and the filler is 20% glass fiber reinforced material. This product is available in Europe or Asia Pacific,. Toyolac®The main features of 100G-20 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 1 | 110 | MPa | ASTM D638 |
| Fracture | 95.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 2 | 3.0 | % | ASTM D638 |
| Fracture | > 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 3 | 6050 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 150 | MPa | ASTM D790 |
| -- 5 | 156 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 12.7 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 106 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 101 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 MF PRTA011 PR305 MSP | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| TEREZ PA 6 7500 GF30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Idemitsu PS SEHI-103 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| JSR EPR EP33 | JSR Corporation | EPDM | JSR EPR |
| LubriOne™ NN-30CF/15T-02S black | PolyOne Corporation | Nylon 66 | LubriOne™ |