Celstran® PP-GF30-02 AD 3019
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pyygXr_Celstran-PP-GF30-02-AD-3019.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% long glass fiber reinforced polypropylene - UV stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 8690 | MPa | ASTM D638 |
| 23°C | 6410 | MPa | ASTM D638 |
| 93°C | 3790 | MPa | ASTM D638 |
| -- | 6550 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 141 | MPa | ASTM D638 |
| Fracture, 23°C | 108 | MPa | ASTM D638 |
| Fracture, 93°C | 66.9 | MPa | ASTM D638 |
| Fracture | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 2.1 | % | ASTM D638 |
| Fracture, 23°C | 2.4 | % | ASTM D638 |
| Fracture, 93°C | 2.8 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 6500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 200 - 210 | °C | |
| Middle Temperature | 210 - 220 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 230 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C |
| Injection instructions |
|---|
| Feed Temperature: 20 to 50°CZone 4 Temperature: 230 to 240°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 80G14AHS NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| BP Flex A 6310 NAT | Buckeye Polymers, Inc. | TPE | BP Flex |
| apilon 52® TL 50 NS | API SpA | TPU-Polyether | apilon 52® |
| Sylvin 9600-55 Red 6127 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 4000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |