Next Nylon 6 Prime Series NX-01M.WH.
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pyTvYY_Next-Nylon-6-Prime-Series-NX-01M-WH-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Un Filled Milky White Compound Product Applications This Grade is used in all sectors of industry Fasteners, monofilament, strapping, plug,caps and filter bowls Benefits Offering for an excellent strength, toughness and stiffness property as well excellent heat, chemical and abrasion resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.2 | -- | % | |
| Across Flow | 1.2 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.3 | -- | % | |
| Saturation 1 | 8.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 70 | -- | ||
| R-Scale | 105 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 75.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 40 | > 50 | % | ASTM D638 |
| Flexural Modulus | 2700 | 2300 | MPa | ASTM D790 |
| Flexural Strength | 110 | 95.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 78 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 165 | -- | °C | |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 28 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AK8 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| MTEGRITY™ PP Homopolymer PP710 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| Versaflex™ CL40 | PolyOne Corporation | TPE | Versaflex™ |
| Bergamid™ A70 MI40 H NC017 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| LEXAN™ HFD1930 resin | SABIC Innovative Plastics | PC | LEXAN™ |