ECP 110
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | TBA Electro Conductive Products Ltd. |
| Trademark: | ECP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pxviKq_ECP-110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
A wide range of polymer bases are employed to produce conductive plastics, including the polyolefines, nylons and ABS.Typical applications are illustrated using ECP 104 mineral filled conductive polypropylene which can be used to mould a variety of containers for static sensitive devices and PCB handling equipment. The mineral filler produces rigid mouldings with excellent dimensional stability.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.03 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/10.0 kg | 10 | g/10 min | |
| 230°C/5.0 kg | 1.0 | g/10 min |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | |
| Tensile Stress | 24.0 | MPa | |
| Flexural Modulus | 1300 | MPa | |
| Flexural Stress | 34.0 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Charpy Notched Impact Strength | No Break | ||
| Charpy Unnotched Impact Strength | No Break |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 78.0 | °C | |
| 1.8 MPa, Unannealed | 49.0 | °C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProvaMed® TPE 1080 | ACTEGA GmbH | TPE | ProvaMed® TPE |
| RABALON® MJ8301C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| VENYL SWGT400H | AD majoris | Nylon 6 | VENYL |
| Iupilon® RS-3001R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Lustran庐 SAN CN25 | Styrolution | SAN | Lustran® SAN |