Stanyl® TS250F4D
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pwxVhy_Stanyl-TS250F4D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TS250F4D is a Polyamide 46 (Nylon 46) material filled with 20% glass fiber. It is available in Asia Pacific. Important attributes of Stanyl® TS250F4D are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9200 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 4.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | 8.0 | kJ/m² | |
| 23°C | 8.0 | 10 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+10 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 200 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.670 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V912A NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Axiall PVC 1522 | Axiall Corporation | PVC Elastomer | Axiall PVC |
| Hostaform® LX90GC15 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Latiohm 87/28-05 PD01 G/10 | LATI S.p.A. | PC | Latiohm |
| ULTEM™ D9065 resin | SABIC Innovative Plastics | PEI | ULTEM™ |