Lotader® 4503
| Category: | EAA , Ethylene Acrylic Acid Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotader® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pwuiLU_Lotader-4503.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTADER® 4503 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process. Applications LOTADER® 4503 is a versatile adhesive for extrusion lamination, designed as a ready for use resin to be used pure. LOTADER® 4503 gives excellent adhesion to plain, primer-less OPET films as well as to other plastic films like OPP, CPP, OPA and reverse-printed films. It also bonds to easier substrates like PE films, aluminium foil, metalized plastics, paper and board. Typical uses are:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 20.0 | wt% | |
| Maleic Anhydride Content | 0.3 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 25 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 9.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 750 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 20.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 45.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 80.0 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 17.NB | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| Manner Flexible PVC 6926 NA 021 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Moplen HP325M | LyondellBasell Industries | PP Homopolymer | Moplen |
| LEXAN™ CFR9111 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| ICORENE® 1613 BK85 | ICO Polymers EMEA, A Division of A. Schulman | LMDPE | ICORENE® |