Order Products : sales@su-jiao.com
Infino HT-8200G
| Category: | Nylon+PPE , Polyamide + PPE |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pwpOwE_Infino-HT-8200G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HT-8200G is a Polyamide + PPE (Nylon+PPE) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (285°C/5.0 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.40 to 0.49 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.61 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8400 | MPa | ASTM D638 |
| -- | 8800 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 140 | MPa | ASTM D638 |
| Yield | 159 | MPa | ISO 527-2/50 |
| Break 3 | 140 | MPa | ASTM D638 |
| Break | 160 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 5900 | MPa | ASTM D790 |
| -- 6 | 11000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 240 | MPa | ASTM D790 |
| -- 8 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 88 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 69 | J/m | ASTM D256 |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 250 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 254 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 231 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 234 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 248 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 285 to 295 | °C | |
| Front Temperature | 300 to 305 | °C | |
| Nozzle Temperature | 310 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP TPO TPO-3975 UVP 848 GLM | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| NEFTEKHIM PE 4143L (424F5) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Braskem PE ML3600S | Braskem | LLDPE | Braskem PE |
| ESENTTIA 02H84ND | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Petrotene® PP A3 T40 NTLA010 PH320 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |