RTP 3183
| Category: | PFA , Perfluoroalkoxy |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pvqA6W_RTP-3183.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| CLTE - Flow | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.55 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 10 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 20mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 - 416 | °C | |
| Middle Temperature | 343 - 416 | °C | |
| Front Temperature | 343 - 416 | °C | |
| Mold Temperature | 121 - 232 | °C | |
| Injection Pressure | 55.2 - 82.7 | MPa | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® BIO 35LANF30-0.101 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| WONDERLITE® PC-110V | CHI MEI CORPORATION | PC | WONDERLITE® |
| Nymax™ 1010 A Black 13 | PolyOne Corporation | Nylon 6 | Nymax™ |
| Cosmic Epoxy EH21 | Cosmic Plastics, Inc. | Epoxy | Cosmic Epoxy |
| Kimura® K2CD | Precision Polymer Engineering Ltd. | Elastomer, Specialty | Kimura® |