Ultramid® A3Z HP BK20465
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ptCfGp_Ultramid-A3Z-HP-BK20465.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid A3Z HP BK20465 is an unreinforced, impact modified, heat stabilized, high flow PA66 injection molding grade. Ultramid A3Z HP BK20465 offers a unique combination of maximum toughness and impact resistance with excellent high flow processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1900 | 1060 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 50.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 45 | > 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1800 | 880 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 28 | 19 | kJ/m² | |
| 23°C | 90 | 110 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 23 | 18 | kJ/m² | |
| 23°C | 80 | 99 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 64.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Suggested Max Moisture | 0.040 to 0.20 | % | |
| Processing (Melt) Temp | 288 to 305 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 40 to 80 | rpm | |
| Screw Compression Ratio | 3.0:1.0 to 4.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Footwear GF-1831 | S&E Specialty Polymers, LLC | PVC+NBR | S&E Footwear |
| TECHNO AES W210 | Techno Polymer Co, Ltd. | AES | TECHNO AES |
| Axiall PVC 12804 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Lucky Enpla LPC1000EX | Lucky Enpla Co LTD | PC | Lucky Enpla |
| Sylvin 6230-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |