Ultramid® Endure D5G3 BM BK20560
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | psi9Kq_Ultramid-Endure-D5G3-BM-BK20560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Endure D5G3 BM BK20560 is a glass fiber reinforced blow molding grade with good sagging behavior, ideal swelling and excellent heat aging resistance up to at least 220 degC (428 degF). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 4.4 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 48 | kJ/m² | |
| 23°C | 84 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| CLTE | |||
| Flow | 3.3E-5 to 3.4E-5 | cm/cm/°C | |
| Transverse | 9.5E-5 to 1.3E-4 | cm/cm/°C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Drying Temperature | 71 | °C | |
| Blow Molding Drying Time | 2.0 to 4.0 | hr | |
| Blow Molding Melt Temperature | 270 to 290 | °C | |
| Blow Molding Moisture Content | 0.15 | % | |
| Blow Molding Mold Temperature | 60 to 90 | °C | |
| Blow-up Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 10 DEL | RTP Company | Acetal (POM) Copolymer | RTP |
| ENVIROPLAS® ENV08-NC870 | ENVIROPLAS®, Inc. | PBT | ENVIROPLAS® |
| Karina LILAC PVC COMPOUND 831-34/148-IS RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ ZX05043 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ STAT-KON™ |
| LOXIM 200 00 V0 | LOXIM Industries Private Limited | PBT | LOXIM |