Eltex® PF6220KJ
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | psbM1g_Eltex-PF6220KJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Benefits & Features Eltex® PF6220KJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties:
Eltex® PF6220KJ offers high slip film with easy opening properties. Addition of other polymers, masterbatch and pigments may alter film slip and antiblock performance. Applications Eltex® PF6220KJ has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex ® PF6220KJ offers easy extrudability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | < 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm | 160 | MPa | |
| 1% Secant, TD : 25 µm | 195 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 9.00 | MPa | |
| TD : Yield, 25 µm | 10.0 | MPa | |
| MD : Break, 25 µm | 60.0 | MPa | |
| TD : Break, 25 µm | 60.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 620 | % | |
| TD : Break, 25 µm | 700 | % | |
| Dart Drop Impact (25 µm) | 1000 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 220 | g | |
| TD : 25 µm | 450 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 1 | 104 to 116 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 60 | ASTM D2457 | |
| Haze (25.0 µm) | 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® S4750 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Wellamid® GF30-60 42LH-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| AKROMID® B3 GF 40 black (3383) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| KYOCERA KE-G240V | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| VALOX™ V3900WX resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | VALOX™ |