Order Products : sales@su-jiao.com

Jam 524F2

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Jam Petrochemical Company
Trademark:	Jam
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ppcYzu_Jam524F2.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Grade under final development, to be industrialised.

Properties on compression moulded specimen according to method MA 17102 (in general agreement with (ASTM D 1928), unless specified.

The density corresponds to the basic grade product, after additivation the density is increased depending on the type of additivation. ESCR made on blow moulded bottles, 1 litre, Basell internal method.

Applications

Blow Moulding

Small Containers

General Information
Uses	Blow molding applications Container
Processing Method	Blow molding

Physical	Nominal Value	Unit	Test Method
Density	0.952	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.25	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (Compression Molded)	30.0	hr	Internal method
Flow Rate Ratio - Compression molded	> 90.0		ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield, molding	27.0	MPa	ASTM D638
Molding	32.0	MPa	ASTM D638
Tensile Elongation (Break, Compression Molded)	850	%	ASTM D638
Flexural Modulus (Compression Molded)	1250	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, Compression Molded)	150	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	127	°C	ASTM D1525

Resin Grade	Manufacturer	Category	Trademark
ELASTOSIL® LR 3003/40 A/B	Wacker Chemie AG	Silicone	ELASTOSIL® LR
Hangzhou Plastic PVC Rigid Film	Hangzhou Plastic Industry Co., Ltd.	Film, PVC	Hangzhou Plastic
Karina CLEAR PVC COMPOUND 87/201-IS-BZ	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
POCAN® DP 2004 000000	LANXESS GmbH	PBT	POCAN®
Sylvin 9812-65 Grey 9558	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin