LNP™ VERTON™ MX02795 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ppLQxs_LNPVERTONMX02795compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON MX02795 is a compound based on Polypropylene resin containing Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized. Also known as: LNP* VERTON* Compound PDX-M-02795 Product reorder name: MX02795 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.53 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.27 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8960 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield | 118 | MPa | ASTM D638 |
| Yield | 111 | MPa | ISO 527-2 |
| Fracture | 118 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield | 2.2 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Fracture | 2.2 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Unnotched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D4812 |
| 23°C 2 | 53 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 7.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 161 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 156 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PC CS500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| BONDYRAM® 7107 | Polyram Ram-On Industries | Nylon, Unspecified | BONDYRAM® |
| Globalprene® 1487 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Hanwha Total PE C430A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| MARPOL® HDM 507-UV | Marco Polo International, Inc. | HDPE | MARPOL® |