Cardia Biohybrid™ BL-F

Category:	TPS+PE , Thermoplastic Starch + PE
Manufacturer:	Cardia Bioplastics™
Trademark:	Cardia Biohybrid™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ppCCuV_Cardia-Biohybrid-BL-F.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Cardia Biohybrid™ BL-F masterbatch is a homogenous blend of thermoplastic starch (TPS) with polyethylene (PE). This blendable grade is compatibilised to offer a high level of mechanical strength, outstanding elongation properties and toughness. The resin is based on corn starch which is a renewable material. This TPS/PE masterbatch can be blended with a wide range of polyolefin materials to tailor a product with properties perfectly matched to the application.

A Biohybrid resin for film applications offering a significant reduction in carbon footprint (compared to PE)

An effective contribution to sustainability where biodegradability/compostability is not required.

Blendable with LDPE, LLDPE, HDPE and PP resins.

Used for thin and thick gauge film and blow moulding applications.

Cardia Biohybrid™ BL-F is formulated with 66% of annually renewable starch. This versatile resin is suitable for a wide range of products manufactured by blown film extrusion and extrusion blow molding as well as injection molding processes. Due its content of polyolefins the material is not a compostable polymer and is not intended for ultimate disposal in commercial composting facilities. For applications in which biodegradability/compostability is required we recommend the usage of Cardia Compostable B-F resin.
Application Examples

Shopping bags/Check-out bags

Garbage bags

Leaf litter bags

Bin liners

Overwrap Packaging

Disposable or industrial bottles

General Information
Features	High strength Updatable resources Good toughness Biodegradable Compliance of Food Exposure Extended tensile rate
Uses	Packaging Films Lining Blow molding applications Bags Mixing Masterbatch Bottle Heavy packing bag
Agency Ratings	European 2002/72/EC
Processing Method	Blow film Blow molding Extrusion blow molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.18	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.2	g/10 min	ASTM D1238
Moisture Content		%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tear Resistance (30.0 µm)	130	N	ASTM D1922

Additional Information	Nominal Value	Unit
Biobased Content - Starch	66	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D883
Yield, 0.0300mm	> 25.0	MPa	ASTM D883
Fracture, 0.0300mm	> 20.0	MPa	ASTM D883
Tensile Elongation (Break, 0.0300 mm)	> 330	%	ASTM D883

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	30	µm
Dart Drop Impact (30 µm)	200	g	ASTM D1709

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	90.0 - 100	°C	ASTM D3418

Additional Information	Nominal Value	Unit
Above film properties are based on a 30µm blown film made from a blend of 50% BLF, 30% LLDPE and 20% LDPE

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU P895RSUA	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
Vydyne® 25WSP	Ascend Performance Materials Operations LLC	Nylon 66	Vydyne®
LubriOne™ NL-30CF/15T Black	PolyOne Corporation	Nylon 612	LubriOne™
TOTAL Polyethylene TPSeal® M 3670	TOTAL Refining & Chemicals	mPE	TOTAL Polyethylene
3M™ Dyneon™ Fluoroelastomer FT 2481	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer