Moplen EP341S

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	LyondellBasell Industries
Trademark:	Moplen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pn4fNF_Moplen-EP341S.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LyondellBasell Australias polypropylene grade EP341S is a high flow impact copolymer with a modified molecular weight distribution and is formulated with a general-purpose additive package. EP341S also contains nucleation additives. EP341S is designed for injection moulding applications requiring excellent mould filling properties, low warpage, and good impact strength at low part weight. End use products typically made from EP341S include thin walled freezer packaging ware and medium to large industrial mouldings.

General Information
Additive	Nucleating agent
Features	Nucleated Low warpage Impact copolymer Impact resistance, good Good formability High liquidity Compliance of Food Exposure
Uses	Thin wall container Industrial application Food container
Agency Ratings	FDA 21 CFR 176.170(c), Table 2, Cond. C FDA 21 CFR 176.170(c), Table 2, Cond. D FDA 21 CFR 176.170(c), Table 2, Cond. E FDA 21 CFR 176.170(c), Table 2, Cond. F FDA 21 CFR 176.170(c), Table 2, Cond. G FDA 21 CFR 176.170(c), Table 2, Cond. H FDA 21 CFR 177.1520(a) 3 (i) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.900	g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	35	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	71		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	22.0	MPa	ISO 527-2
Flexural Modulus	1100	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ISO 180/1A
-20°C	2.0	kJ/m²	ISO 180/1A
0°C	3.0	kJ/m²	ISO 180/1A
23°C	4.0	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	75.0	°C	ISO 75-2/B
1.8 MPa, not annealed	50.0	°C	ISO 75-2/A
Vicat Softening Temperature	145	°C	ISO 306/A

Additional Information
Falling Weight Impact Strength @ -40°C, BS2782-306b, 8J

Resin Grade	Manufacturer	Category	Trademark
RTP 1300 C GB 40	RTP Company	PPS	RTP
Telcar® TL-1123 BLK 111	Teknor Apex Company	TPE	Telcar®
Bergamid™ B70 G/GK30 TM-Y UV NC	PolyOne Corporation	Nylon 6	Bergamid™
ISOTHANE® 1080AF	Great Eastern Resins Industrial Co Ltd (GRECO)	TPU-Polyester	ISOTHANE®
LNP™ LUBRICOMP™ HFG25Z compound	SABIC Innovative Plastics	Nylon 11	LNP™ LUBRICOMP™