Staramide RFM3353EM
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pkUIRc_Staramide-RFM3353EM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide* RFM3353EM is a Glass Fiber Reinforced , Mineral Filled, Polyamide 66 / Polyamide 6, Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.20 to 0.50 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 5.1 | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 to 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 250 | °C | ASTM D648 |
| CLTE - Flow (23 to 60°C) | 3.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (1.50 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP502H | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| VITAMIDE® BG32NT6719 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Vyncolit® X659 | Vyncolit N.V. | Phenolic | Vyncolit® |
| ExxonMobil™ PP7815E1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Generic Nylon 66+Nylon 6I/X | Generic | Nylon 66+Nylon 6I/X | Generic |