This data represents typical values that have been calculated from all products classified as: Generic ABS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 - 1.11 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.11 | g/cm³ | ISO 1183 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| -- | 1.01 - 1.10 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.25 - 0.36 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 1.0 - 36 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 0.49 - 36 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 220°C/10.0 kg | 1.30 - 41.2 | cm³/10min | ISO 1133 |
| -- | 22.3 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.45 - 0.74 | % | ASTM D955 |
| Transverse flow : 23°C | 0.37 - 0.91 | % | ASTM D955 |
| 23°C | 0.48 - 0.71 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.20 - 0.31 | % | ASTM D570 |
| 23°C, 24 hr | 0.26 - 0.31 | % | ISO 62 |
| Saturated, 23°C | 0.30 - 1.0 | % | ASTM D570 |
| Saturated, 23°C | 0.10 - 1.6 | % | ISO 62 |
| Saturation | 0.19 | % | ISO 62 3 |
| Equilibrium, 23°C | 0.30 - 0.31 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 - 0.37 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 97 - 115 | ASTM D785 | |
| 23°C | 95 - 117 | ISO 2039-2 | |
| Ball Indentation Hardness | 74.0 - 111 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1700 - 2830 | MPa | ASTM D638 |
| 23°C | 1730 - 2760 | MPa | ISO 527-2 |
| -- | 2150 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 23°C | 34.1 - 51.2 | MPa | ASTM D638 |
| Yield, 23°C | 35.8 - 63.5 | MPa | ISO 527-2 |
| Yield | 41.6 | MPa | ISO 527-2 5 |
| Fracture, 23°C | 26.4 - 50.1 | MPa | ASTM D638 |
| Fracture, 23°C | 28.9 - 41.9 | MPa | ISO 527-2 |
| 23°C | 32.1 - 53.5 | MPa | ASTM D638 |
| 23°C | 40.0 - 48.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 2.0 - 12 | % | ASTM D638 |
| Yield, 23°C | 1.8 - 3.6 | % | ISO 527-2 |
| Yield | 5.0 | % | ISO 527-2 6 |
| Fracture, 23°C | 1.0 - 57 | % | ASTM D638 |
| Fracture, 23°C | 4.6 - 27 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | |||
| 23°C | 8.8 - 36 | % | ISO 527-2 |
| -- | 16 - 50 | % | ISO 527-2 7 |
| Flexural Modulus | |||
| 23°C | 1540 - 2880 | MPa | ASTM D790 |
| 23°C | 1860 - 2860 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 52.0 - 81.6 | MPa | ASTM D790 |
| 23°C | 54.0 - 86.0 | MPa | ISO 178 |
| Yield, 23°C | 54.8 - 77.5 | MPa | ASTM D790 |
| Fracture, 23°C | 53.9 - 72.8 | MPa | ASTM D790 |
| Coefficient of Friction | 0.080 - 0.46 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 5.6 - 30 | kJ/m² | ISO 179 |
| -30°C | 8.46 | kJ/m² | ISO 179/1eA 8 |
| 23°C | 35.9 | kJ/m² | ISO 179/1eA 9 |
| Charpy Unnotched Impact Strength (23°C) | 6.0 - 180 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 92 - 410 | J/m | ASTM D256 |
| 23°C | 9.0 - 37 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 59 - 1600 | J/m | ASTM D256 |
| 23°C | 6.8 - 100 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 2.82 - 39.6 | J | ASTM D3763 |
| 23°C | 3.85 - 33.0 | J | ISO 6603-2 |
| Dart Drop Impact (23°C) | 2.71 - 40.5 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 81.5 - 100 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 71.8 - 105 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 98.7 - 103 | °C | ASTM D648 |
| 0.45 MPa, annealed | 85.0 - 109 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 74.3 - 101 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.8 - 99.8 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 84.9 - 100 | °C | ASTM D648 |
| 1.8 MPa, annealed | 89.6 - 101 | °C | ISO 75-2/A |
| Continuous Use Temperature | 60.0 - 75.0 | °C | ASTM D794 |
| Glass Transition Temperature 10 | 110 | °C | ISO 11357-2 11 |
| Vicat Softening Temperature | |||
| -- | 83.6 - 116 | °C | ASTM D1525 |
| -- | 87.6 - 110 | °C | ISO 306 |
| 50°C/h, B (50N) | 94.6 | °C | ISO 306 12 |
| Ball Indentation Temperature | 75.0 - 80.3 | °C | IEC 60598-1 |
| Linear thermal expansion coefficient | |||
| Flow | 7.9E-5 - 9.1E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flow | 7.6E-5 - 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flow | 8.2E-5 | cm/cm/°C | ISO 11359-2 13 |
| Lateral | 7.9E-5 - 1.2E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 5.8E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.9E-5 | cm/cm/°C | ISO 11359-2 14 |
| Specific Heat (23°C) | 1660 - 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | |||
| 23°C | 0.15 - 0.22 | W/m/K | ASTM C177 |
| 23°C | 0.17 - 0.18 | W/m/K | ISO 8302 |
| RTI Elec | 59.0 - 61.3 | °C | UL 746 |
| RTI Imp | 58.8 - 60.5 | °C | UL 746 |
| RTI | 59.0 - 61.3 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 4.0 - 1.0E+15 | ohms | ASTM D257 |
| -- | 1.0E+10 - 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 0.15 - 1.3E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+12 - 2.5E+16 | ohms·cm | IEC 60093 |
| -- | 9.8E+12 - 1.0E+13 | ohms·m | IEC 60093 15 |
| Dielectric Strength | |||
| 23°C | 15 - 35 | kV/mm | ASTM D149 |
| 23°C | 24 - 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.80 - 3.21 | ASTM D150 | |
| 23°C | 3.10 - 3.20 | IEC 60250 | |
| 23°C | 2.95 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 4.0E-3 - 0.015 | ASTM D150 | |
| 23°C | 4.8E-3 - 0.015 | IEC 60250 | |
| Arc Resistance | 5.00 - 8.88 | sec | ASTM D495 |
| Comparative Tracking Index | 581 - 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | 195 - 200 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | 0.00 - 3.73 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | 13 - 34 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 36 - 69 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 642 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 - 27 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 59 - 99 | ASTM D523 | |
| Gloss | 30 - 100 | ASTM D2457 | |
| Transmittance | 86.0 - 93.0 | % | ASTM D1003 |
| Haze | 1.5 - 4.0 | % | ASTM D1003 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 155 - 1550 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.5 - 89.3 | °C | |
| Drying Time | 2.2 - 3.7 | hr | |
| Drying Time, Maximum | 7.5 | hr | |
| Dew Point | -18.8 - -17.3 | °C | |
| Suggested Max Moisture | 0.010 - 0.16 | % | |
| Suggested Shot Size | 55 - 63 | % | |
| Suggested Max Regrind | 13 | % | |
| Hopper Temperature | 70.0 - 245 | °C | |
| Rear Temperature | 169 - 245 | °C | |
| Middle Temperature | 189 - 246 | °C | |
| Front Temperature | 194 - 252 | °C | |
| Nozzle Temperature | 208 - 254 | °C | |
| Processing (Melt) Temp | 208 - 261 | °C | |
| Melt Temperature (Aim) | 233 | °C | |
| Mold Temperature | 49.0 - 71.4 | °C | |
| Injection Pressure | 4.08 - 107 | MPa | |
| Holding Pressure | 3.43 - 52.9 | MPa | |
| Back Pressure | 0.00500 - 45.1 | MPa | |
| Screw Speed | 44 - 76 | rpm | |
| Clamp Tonnage | 4.1 - 4.5 | kN/cm² | |
| Cushion | 3.18 - 9.53 | mm | |
| Vent Depth | 0.044 - 0.045 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABSThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 90.6 | °C | |
| Drying Time | 2.8 - 3.7 | hr | |
| Suggested Max Moisture | 8.5E-3 - 0.076 | % | |
| Cylinder Zone 1 Temp. | 170 - 231 | °C | |
| Cylinder Zone 2 Temp. | 199 - 211 | °C | |
| Cylinder Zone 3 Temp. | 200 - 226 | °C | |
| Cylinder Zone 4 Temp. | 199 - 225 | °C | |
| Cylinder Zone 5 Temp. | 199 - 236 | °C | |
| Adapter Temperature | 212 - 232 | °C | |
| Melt Temperature | 196 - 246 | °C | |
| Die Temperature | 214 - 226 | °C | |
| Take-Off Roll | 70.0 - 95.0 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABSThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | 10 °C/min |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Nylon A4TR01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| Zetpol® 1020 | Zeon Corporation | NBR | Zetpol® |
| Next Nylon 66 Prime Series PGF25-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Guang Sung PVC GPMA70 | Guang Sung Plastics (GSPL) | PVC, Flexible | Guang Sung PVC |
| Estane® 2355-95AEF TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |