LNP™ LUBRICOMP™ EX07305 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pivGW8_LNP-LUBRICOMP-EX07305-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyetherimide reinforced with Glass fiber and PTFE for use in Burn-in Test Sockets (BiTS) Application |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.40 | % | |
| Across Flow | 0.52 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8630 | MPa | ASTM D638 |
| -- | 8550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 157 | MPa | ASTM D638 |
| Break | 156 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.0 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6420 | MPa | ASTM D790 |
| -- 5 | 7220 | MPa | ISO 178 |
| Flexural Strength 6 | ASTM D790 | ||
| Yield, 50.0 mm Span | 202 | MPa | |
| Break, 50.0 mm Span | 201 | MPa | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.52 | ASTM D3702 Modified | |
| Wear Factor - Washer | 15.6 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 67 | J/m | ASTM D256 |
| 23°C 7 | 7.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 8 | 26 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 207 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 7.6E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm, in Oil) | 31 | kV/mm | ASTM D149 |
| Dielectric Constant (100 kHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (100 kHz) | 3.1E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 805 HB | RTP Company | Acetal (POM) Copolymer | RTP |
| Xuchuan XCW-20N | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| KMI PC 101HMB | KMI Group Inc. | PC | KMI PC |
| Iupiace® LGX420N | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Sylvin 916VO-95 Green 3108 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |