Zytel® E51HSB NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pgyo5p_Zytel-E51HSB-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, Heat Stabilized, High Viscosity Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 8.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.6 | -- | % | |
| Viscosity Number | 330 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 84.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.3 | 29 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 35 | -- | % | ISO 527-2 |
| Flexural Modulus | 2800 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 4.0 | kJ/m² | |
| 23°C | 7.0 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 221 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Oxygen Index | 20 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 0.980 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2790 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PP ABS HI112H | Performance Plastics, Ltd. | ABS | PP ABS |
| RTP ESD C 0280 FR | RTP Company | Nylon 66 | RTP |
| Chansieh Phenolic J-263-1 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| Clariant Nylon 6/6 PA-113N40 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Paracril® X3675 | INSA | NBR | Paracril® |