Novalloy-B B5723
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pgaG1E_NovalloyBB5723.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-B B5723 is an acrylonitrile butadiene styrene + PBT (ABS + PBT) material, and its filler is 15% glass fiber reinforced material. This product is available in the Asia-Pacific region,. The main characteristics of Novalloy-B B5723 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 91.0 | MPa | ISO 527-2 |
| Flexural Modulus | 5600 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 210 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 185 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 175 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.50 mm) | 29 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 3 | UL 746 | |
| Comparative Tracking Index (3.00 mm) | 225 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) (1.50 mm) | 25.0 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 87.0 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 27 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 230 - 250 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 5.00 - 20.0 | MPa | |
| Screw Speed | 50 - 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYLOPET® EMC333 | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| 3M™ Dyneon™ PTFE Compound TF 4303 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LARIPUR® LPR 6520 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| ICORENE® 9033 BA8 | ICO Polymers SA, A Division of A. Schulman | PE, Unspecified | ICORENE® |
| MAJORIS EB760 | AD majoris | PP, Unspecified | MAJORIS |