ACLAR® 33C (7.8 mil)
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pfLDaf_ACLAR-33C-7-8-mil-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar 33C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). 33C 7.80 mil combines outstanding moisture barrier with excellent chemical resistance and mechanical strength. 33C is used for military and industrial packaging applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.12 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 200 µm | 1330 | MPa | ASTM D882 |
| TD : 200 µm | 1330 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 200 µm | 27.0 | MPa | ASTM D882 |
| TD : Yield, 200 µm | 24.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 200 µm | 87 | % | ASTM D882 |
| TD : Yield, 200 µm | 87 | % | ASTM D882 |
| Water Vapor Transmission Rate (200 µm, 38°C, 100% RH) | 0.050 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 206 | °C | ASTM D3418 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (0.198 mm) | 100 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (198 µm) | < 4.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 2.38 m²/kgTear Strength, ASTM D1004, Graves MD: 425 to 525 g/milTear Strength, ASTM D1004, Graves TD: 425 to 525 g/milCrystalline Melting Point, ASTM D4591: 206 °CDimensional Stability, ASTM D1204, 10 min, 300°F, MD: |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNILID 1250 | Tekni-Films, a div of Tekni-Plex | Film, Coated Al Foil | TEKNILID |
| KumhoSunny PC/ABS HAC8265H | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Karina IVORY PVC COMPOUND -E 60820-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ FX93387L compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ THERMOCOMP™ |
| Daelim Po1y® XP9200 | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |