LUVOCOM® 1106-8465 Datasheet,PEI,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1106-8465 is a polyetherimide (PEI) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1106-8465 are: flame retardant/rated flame Conductivity Flame Retardant Good stiffness Heat resistance LUVOCOM®The typical application areas of 1106-8465 are: electrical/electronic applications

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Features	Conductivity Heat conduction Rigid, good Static conduction Antistatic property Good strength Heat resistance, high Flame retardancy
Uses	Electrical/Electronic Applications
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.43	g/cm³	ISO 1183
Molding Shrinkage	0.10 - 0.30	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.20	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	21000	MPa	ISO 527-2
Tensile Stress (Break)	125	MPa	ISO 527-2
Tensile Strain (Yield)	0.80	%	ISO 527-2
Flexural Modulus	18000	MPa	ISO 178
Flexural Stress	180	MPa	ISO 178
Flexural Strain at Flexural Strength	0.90	%	ISO 178

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	14	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	200	°C	ISO 75-2/A
Continuous Use Temperature	170	°C	UL 746B
CLTE - Flow	8.0E-6	cm/cm/°C	DIN 53752
Thermal Conductivity ¹	6.0	W/m/K

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+5	ohms	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating ²	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	120	°C
Hot air dryer, B	150	°C
Drying Time
Hot air dryer, A	> 8.0	hr
Hot air dryer, B	> 4.0	hr
Rear Temperature	330 - 350	°C
Middle Temperature	340 - 390	°C
Front Temperature	350 - 400	°C
Nozzle Temperature	350 - 400	°C
Processing (Melt) Temp	380	°C
Mold Temperature	150 - 180	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Note Message
1 .	Hot-Disk, 60x60x3 mm
2 .	Not recognized by UL.

Category:	PEI , Polyether Imide
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	pfH84F_LUVOCOM11068465.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
REPOL® C120MN	Reliance Industries Limited	PP Impact Copolymer	REPOL®
NuSil MED-4780	NuSil Technology	Rubber	NuSil
CERTENE™ 705 SAN	Muehlstein	SAN	CERTENE™
Hanwha Total PP TB53T	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP
Karina CLEAR PVC COMPOUND 75/201-D-AT-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina