Radel® R-5800

Category:	PPSU , Polyphenylsulfone
Manufacturer:	Solvay Specialty Polymers
Trademark:	Radel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	peDb9m_Radel-R-5800.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Radel® R-5800 is a high melt flow grade of Radel® polyphenylsulfone (PPSU). It is especially well-suited for parts requiring long flow length with thin walls. Radel® resins offer exceptional hydrolytic stability and toughness superior to other commercially-available, high-temperature engineering resins. They also offer high deflection temperatures and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties.

Additonal Radel® grades include a transparent injection molding grade (R-5000), an opaque, general purpose, injection molding grade (R-5100) and a transparent, extrusion grade (R-5500).

Natural/Transparent: Radel® R-5800 NT

Additional Made-to-Order Colors Available

General Information
Features	Acid Resistant Autoclave Sterilizable Base Resistant Biocompatible E-beam Sterilizable Ethylene Oxide Sterilizable Flame Retardant Good Chemical Resistance Good Sterilizability Good Thermal Stability Heat Sterilizable High ESCR (Stress Crack Resist.) High Heat Resistance Hydrolytically Stable Radiation (Gamma) Resistant Radiation Sterilizable Radiotranslucent Steam Resistant Steam Sterilizable Ultra High Toughness
Uses	Aerospace Applications Aircraft Applications Automotive Applications Dental Applications Food Service Applications Hospital Goods Medical Devices Medical/Healthcare Applications Surgical Instruments
Agency Ratings	ISO 10993
RoHS Compliance	RoHS Compliant
Appearance	Clear Amber Colors Available
Forms	Pellets
Processing Method	Extrusion Injection Molding Sheet Extrusion Thermoforming
Multi-Point Data	Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.29	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (365°C/5.0 kg)	20 to 28	g/10 min	ASTM D1238
Molding Shrinkage - Flow (3.18 mm)	0.70	%	ASTM D955
Water Absorption			ASTM D570
24 hr	0.37	%
Equilibrium	1.1	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (3.18 mm)	2340	MPa	ASTM D638
Tensile Strength (3.18 mm)	69.6	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield, 3.18 mm	7.2	%
Break, 3.18 mm	60 to 120	%
Flexural Modulus (3.18 mm)	2410	MPa	ASTM D790
Flexural Strength (5.0% Strain, 3.18 mm)	91.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	690	J/m	ASTM D256
Tensile Impact Strength (3.18 mm)	399	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm)	207	°C	ASTM D648
Glass Transition Temperature ¹	220	°C	DSC
CLTE - Flow (3.18 mm)	5.6E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity (3.18 mm)	9.0E+15	ohms·cm	ASTM D257
Dielectric Strength			ASTM D149
0.0254 mm	> 200	kV/mm
3.18 mm	15	kV/mm
Dielectric Constant (3.18 mm, 60 Hz)	3.44		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating ²(0.762 mm)	V-0		UL 94

Optical	Nominal Value		Test Method
Refractive Index	1.672		ASTM D542

Additional Information	Nominal Value	Unit
Steam Sterilization - w/ Morpholine ³	> 1000	Cycles

Injection	Nominal Value	Unit
Drying Temperature	149	°C
Drying Time	2.5	hr
Processing (Melt) Temp	360 to 391	°C
Mold Temperature	138 to 163	°C
Screw Compression Ratio	2.2:1.0

Extrusion	Nominal Value	Unit
Drying Temperature	171	°C
Drying Time	4.0	hr

Note Message
1 .	Heating rate of 36°F (20°C) per minute.
2 .	These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions.
3 .	Cycles passed without cracking, crazing, or rupture.Steam Autoclave Conditions:- Temperature: 270°F (132°C)- Time: 30 minutes/cycle- Steam Pressure: 27 psig (0.19 MPa)- Stress Level: 1000 psi (7.0 MPa) in flexure- Additive: Morpholine at 50 ppm

Resin Grade	Manufacturer	Category	Trademark
Veroplas K160	PlastxWorld Inc.	Acrylic (PMMA)	Veroplas
Niche PPCT20BK	Niche Polymer, LLC	PP Copolymer	Niche
NYCOA Polyamide 471	Nycoa (Nylon Corporation of America)	Nylon 6	NYCOA Polyamide
ELASTOSIL® E 60	Wacker Chemie AG	Silicone	ELASTOSIL® E
POCAN® B 3215 XF 000000	LANXESS Asia/Pacific	PBT	POCAN®