Veradel® 3300 PREM MR
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Veradel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | peCTtT_Veradel3300PREMMR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Veradel®PESU originally used Gafone™PESU sales. Veradel polyethersulfone (PESU) is transparent, has high thermal deformation temperature, excellent toughness and dimensional stability, and is resistant to water vapor, boiling water and inorganic acid. Other excellent properties include thermal stability, creep resistance and inherent flame retardancy. 3200 Veradel meet FDA standards and can come into direct contact with food. The Veradel 3200 is a low melt flow rate grade, both extrusion and injection molding. The Veradel 3300 is a medium melt flow rate grade and is recommended for conventional injection molding. Veradel 3400 is a high melt flow rate grade, suitable for thin-walled or long flow distance components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Water Absorption - 30 days | 1.9 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D638 |
| Tensile Strength | 88.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 200 | °C | ASTM D648 |
| CLTE - Flow | 5.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.7E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.51 | ASTM D150 | |
| 1 kHz | 3.50 | ASTM D150 | |
| 1 MHz | 3.54 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.7E-3 | ASTM D150 | |
| 1 kHz | 2.2E-3 | ASTM D150 | |
| 1 MHz | 5.6E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(1.5 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 2.5 | hr | |
| Processing (Melt) Temp | 343 - 385 | °C | |
| Mold Temperature | 149 - 163 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0:1.0 |
| Note Message | |
|---|---|
| 1 . | These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 3152 | Covestro - Polycarbonates | PC | Makrolon® |
| Toraypef® 20020 AP66 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| KOPA® KN1133W | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Medalist® MD-53288 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |
| Sylvin 8496-70FUV Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |