CoolPoly® D5108
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pdzxix_CoolPoly-D5108.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.82 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 37.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.16 | % | ISO 527-2 |
| Flexural Modulus | 19400 | MPa | ISO 178 |
| Flexural Stress | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 2.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 276 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 239 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.5E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 10 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.5E+14 | ohms | ASTM D257 |
| Volume Resistivity | 2.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 29 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.80 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 0.022 | ASTM D150 | |
| 1 MHz | 2.3E-3 | ASTM D150 | |
| Arc Resistance | 300 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 580 | V | UL 746 |
| Hot-wire Ignition (HWI) | 120 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Nominal Tensile Strain at Break, ISO 527-1, -2, was tested in accordance with ASTM D412.The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461.The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551.The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461.Thermal Diffusivity, ASTM E1461: 0.07 cm²/secComparative Tracking Index, ASTM 3638: 580 voltsHot Wire Ignition, ASTM D3874: >120 secHigh Voltage Arc Tracking Rate, UL-746A: did not trackHigh Voltage Arc Resistance to Ignition, UL-746A: >300 sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Suggested Max Moisture | 0.0 | % | |
| Rear Temperature | 290 - 315 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 310 - 340 | °C | |
| Nozzle Temperature | 316 - 340 | °C | |
| Processing (Melt) Temp | 307 - 338 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 60.0 - 165 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 105 | MPa | |
| Back Pressure | 0.200 - 0.500 | MPa | |
| Screw Speed | 75 - 180 | rpm | |
| Cushion | 5.00 - 13.0 | mm | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 85860 B | RTP Company | PP, Unspecified | RTP |
| POLYPRO® 5014L | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Braskem PE IDEALIS500 | Braskem America Inc. | HMWPE | Braskem PE |
| Desmopan® DP 9392A | Covestro - PUR | TPU, Unspecified | Desmopan® |
| LEXAN™ LUX7636C resin | SABIC Innovative Plastics | PC | LEXAN™ |